1.Product Introduction
EVA film for super Clearsafety glass is made of high quality, visual transparent polyestermaterial processed by special equipment. It has the characteristics of toughness, high transparency, highbonding strength, high elongation, good low temperature resistance and so on. It is an ideal bonding material for laminating safety glass in the world. The glass can be widely used in curtain wall, sunshine room, guardrailstaircase handrail and other special glass production fields. Our film has passed the test by China national safetyglass & quartz glass test center and fully in line with the standard of GB 9962-1999.
| Product name | Thickness(mm) | Width(mm) | Length(m) | Scope of application |
| Super Clear EVA film | 0.38 | 500-2650 | 100 | Application: Curtain wall, sun room, top floor, stair handrail and other tempered glass lamination (suitable for tempered glass that is not smooth, or has special shapes or depressions) Also suitable for "shower room" high transparency lamination and gradient film lamination and landscape painting glass processing |
| 0.5 | 500-2700 | 80 |
| 0.76 | 500-2700 | 50 |
| 1.14 | 500-2700 | |
| 1.52 | 500-2700 | |
2.Product detailed parameters
| 项目 Item | 单位Unit | 性能指标 Performance Index |
| 熔点 Melting Point | ℃ | 66 |
| 密度 Density | g / cm³ | 0.954 |
| 玻璃化温度 Glass Transition Temp | ℃ | -45 |
| 拉伸强度 Tensile Strength | Mpa | 24.9 |
| 断裂伸长率 Elongation (before laminated) | % | 811 |
| 交联度 Degree if crosslinking | % | 75 |
| 吸水率 Water absorption | % | <=0.1 |
| 雾度 Haze | % | 0.31 |
| 透光率 Light Transmittance | % | 91.4 |
| 粘结强度(玻璃) Bonding Strength (glass) | N / 10mm | 98 |
| 紫外线阻隔率 UV reduction | % | >=99 |
| 耐紫外线老化 UV aging resistance (15Kwh / m2、290~385nm) | 透光率%Light Transmittance% | 88.3 |
| 耐湿热老化 Damp&heataging( 85℃85%湿度humidity1000h) | 透光率%Light Transmittance% | 86.2 |
| 散弹袋冲击性能 Impact resistance against shot-bag GB-15763.3-2009 | 1200MM | 两面玻璃破裂，无穿透性开口 Qualified |
| 落球冲击试验 Ball impact resistance GB-15763.3-2009 | 4800MM | 胶层为断裂、未暴露 Qualified |
| 耐湿性 Humidity aging resistance GB-15763.3-2009 | | 未产生气泡或其他缺陷Qualified |
3.Processing Technic
Note:
1)After combining the glass, old pumping 10 mins. Taking glass temperature as the criterion, and the temperature of high temperature period can’t less than 125℃.
2)Increase keeping time if glass thickness increased or SQM increased.
4.Application Cases
5.Packaging and transportation
precautions
1) EVA laminated glass adhesive film is usually required to be stored in a ventilated, dry, and clean warehouse, avoiding direct radiation from light and heat sources; Prevent rain, heavy pressure, external impact, and scratches from hard objects; The temperature in the warehouse should not exceed 30 ℃, and the humidity should not exceed 60%; When there is a large inventory of film, a tray should be placed under the film to facilitate ventilation, heat dissipation, and moisture isolation. If the film is subjected to pressure, heat, or excessive moisture, it may exhibit varying degrees of self adhesion. If possible, please hang it for storage and avoid heavy pressure as much as possible. If the surface humidity of the adhesive film is too high, it will also affect the bonding strength between the adhesive film and glass or other adhesives, affecting normal use.
2)EVA laminated glass film is prohibited from being stored in the same warehouse as flammable and explosive materials; The remaining film after use must be repackaged with clean materials to prevent the weak static electricity carried by the film itself from adsorbing dust and contaminating the film, affecting normal use.
3) EVA laminated glass film has an “effective storage period” of ten months from its production. Customers with inventory turnover must perform a rolling operation of “storing new and using old”. If customers use film that has exceeded the storage period for production and processing, we are not responsible for the quality of their products. If the film purchased by the customer has not been used for a long time and the storage period has exceeded the “effective storage period”, regardless of whether there are inherent quality problems with the product, we will not process returns or exchanges.
6.Special Warning
Whether it is EVA film or intermediate materials (such as photo paper), due to improper storage, there will be “discharge” phenomenon in rainy and humid weather. Even if glass appears, there will still be a thin layer of water mist floating on the surface of the glass. If this “moisture” phenomenon is not ruled out, the bonding strength of tempered glass after processing and forming will be greatly affected. Therefore, customers are advised to avoid high humidity weather during production. Proper drying of materials and glass is beneficial for improving bonding strength.